Reinforced,reinforced flame retardant PET offers good mechanical properties,good fatigue resistance,thermooxidizing resistance,soldering resisance,good dielectric strength,good flow and processibility;good flammability after joined flame retardant agent.
Reinforced,reinforced flame retardant PET is used for household electric appliance parts,communications, equipments,printed plate board,rectifier parts,indestrial switchboard,electrical appliances with inlays,electric coil skeleton,integrated circuit parts,automobile electyical appliances,etc.
Properties | Test Method ASTM | Unit | PET Increase ¡¢Flame | ||
G20S | G30S | G30FR | |||
Density | D792 | g/cm3 | 1.55 | 1.6 | 1.65 |
Tensile Strength | D638 | MPa | 160 | 175 | 150 |
Tensile Elongation | D638 | % | 2.0 | 1.7 | 3.5 |
Flexural Strength | D790 | MPa | 230 | 240 | 225 |
Flexural Modulus | D790 | MPa | 9700 | 9800 | 9600 |
Notched Charpy Impact Strength | D256 | KJ/m2 | 9.0 | 9.7 | 8.5 |
Heat Deflection Temperature 1.86MPa | D648 | ¡æ | 242 | 247 | 240 |
Vicat Softening Point | D1525 | ¡æ | |||
Flame Resistance Properties 3.2mm | UL94 | HB | HB | V-0 | |
1.6mm | UL94 | HB | HB | V-0 | |
Melt Index | D1238 | g/10min | |||
Volume Resistivity | D257 | ¦¸.cm | 1015 | 1015 | 1015 |
Molding Shrinkage | D955 | % | 0.3~0.9 | 0.3~0.7 | 0.3~0.6 |
Note | GF20% | GF30% | GF30% |
The details given in this data sheet are our laboratory data but not specification guaranteed.
einforced,reinforced flame retardant PET processing conditions: injection temperature 250~285¡æ, mold temperature 60~100¡æ,injection pressure 80~120MPa, eliminate moisture at 125~130¡æ for 5~8 hours.